| ACRYPET® MD是一种聚甲基丙烯酸甲酯-丙烯酸材料,。 该产品在北美洲或亚太地区有供货,。 ACRYPET® MD的主要特性为:紫外线稳定。 ACRYPET® MD的典型应用领域为:汽车行业 |
| Product Description | |
|---|---|
| Supplier | Mitsubishi |
| Generic | PMMA |
| Material Status | Commercial: Active |
| Availabilitys | North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，3.8kg | 6.0 | g/10min | ISO 1133 |
| Spiral flow length | |||
| — | 19.0 | cm | |
| — | 29.0 | cm | |
| Shrinkage rate | 0.20 to 0.60 | % | Internal Method |
| Water absorption rate | |||
| 23℃，24hr | 0.30 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 1.4 | kJ/m² | ISO 179-1eA |
| Charpy Unnotch Impact strength | 19 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | 2.1 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 87.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 94.0 | ℃ | ISO 306/B |
| Linear coefficient of thermal expansion | |||
| MD | 6.0E-5 | 1/℃ | ASTM D696 |
| specific heat | 1500 | J/kg/°C | JIS K7123 |
| Thermal conductivity coefficient | 0.20 | W/m/K | ASTM C177 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+16 | ohms | JIS K6911 |
| Volume resistivity | > 1.0E+15 | ohms·cm | JIS K6911 |
| Dielectric strength | 20 | kV/mm | JIS K6911 |
| Dielectric constant | |||
| 60 Hz | 3.70 | JIS K6911 | |
| Dissipation factor | |||
| 60 Hz | 0.050 | JIS K6911 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.490 | ASTM D542 | |
| Transmittance | |||
| Total, 3000 µ m | 93.0 | % | ISO 13468 |
| Haze | |||
| 3000 µm | 0.30 | % | ISO 14782 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 94 | ISO 2039-2 | |
| Tensile modulus | 3300 | MPa | ISO 527-2/1A/1 |
| Tensile stress | 71.0 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| fracture | 6.0 | % | ISO 527-2/1A/5 |
| Bending modulus | 3300 | MPa | ISO 178 |
| Bending stress | 130 | MPa | ISO 178 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |