| About |
|---|
| ACRYPET® MF 001 是一种聚甲基丙烯酸甲酯-丙烯酸材料,。 该产品在北美洲、欧洲或亚太地区有供货,。 ACRYPET® MD的主要特性为:紫外线稳定,高流动。 ACRYPET® MF的典型应用领域为:汽车行业 |
| Product Description | |
|---|---|
| Supplier | Mitsubishi |
| Generic | PMMA |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,High liquidity |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ISO 1183 |
| Shrinkage rate | 0.2-0.6 | ||
| Melt Flow Rate | |||
| 230℃，3.8kg | 14 | g/10min | ISO 1133 |
| Water absorption rate | 0.3 | ％ | ISO 62 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| specific heat | 1.5 | J/(g･K) | JIS K7123 |
| Linear coefficient of thermal expansion | 6×10^-5 | 1/℃ | JIS K7197 |
| Heat transfer rate | 0.2 | W/(m･K) | JIS A1412 |
| Hot deformation temperature | |||
| 1.8 MPa | 84 | ℃ | ISO 75 |
| Vicat Softening Temp | 89 | ℃ | ISO 306 |
| Spiral flow (thickness 2mm) | |||
| 230℃ | 250 | mm | |
| 250℃ | 370 | mm |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 66 | MPa | ISO 527 |
| Tensile strain | 4 | ％ | ISO 527 |
| Tensile modulus | 3300 | MPa | ISO 527 |
| bending strength | 120 | MPa | ISO 178 |
| Bending modulus | 3300 | MPa | ISO 178 |
| Rockwell hardness (M-level) | 86 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistance coefficient | >10^16 | Ω | JIS K6911 |
| Volumetric resistance coefficient | >10^13 | Ωm | JIS K6911 |
| Insulation breakdown strength (4kV/sec) | 20 | mV/m | JIS K6911 |
| Dielectric constant | |||
| 60 Hz | 3.7 | JIS K6911 | |
| Dielectric attenuation factor (60Hz) | 0.05 | JIS K6911 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Full light transmittance | 93 | % | ISO 13468 |
| Haze | 0.3 | % | ISO 14782 |
| Refractive index | 1.49 | ISO 489 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.5mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| 1eU | 18 | kJ/m² | ISO 179 |
| 1eA | 1.3 | kJ/m² | ISO 179 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |