| ADDILENE J 490 M20 S是一种聚丙烯材料,含有的填充物为20% 矿物填料。 该产品在亚太地区、拉丁美洲、欧洲或非洲和中东有供货,。 ADDILENE J 490 M20 S的主要特性有: 阻燃/额定火焰 Flame Retardant 典型应用领域包括: 工业应用 房屋 电气/电子应用&& |
| Product Description | |
|---|---|
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,Halogenated,V-2 |
| Availabilitys | Africa & Middle East ,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 230℃，2.16kg | 12 | g/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.5 | kJ/m² | ISO 179-1eA |
| Charpy Unnotch Impact strength | 40 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | 3.5 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 61.0 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| A50 | 151 | ℃ | ISO 306/A50 |
| Melting temperature | |||
| DSC | 165 to 168 | ℃ | ISO 3146 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 43 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | |||
| Solution A | > 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | V-2 | UL 94 | |
| Igniting temperature of the hot wire | 850 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 23 | % | ISO 4589-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 70 | ISO 868 | |
| tensile strength | |||
| fracture | 26.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 13 | % | ISO 527-2 |
| Bending modulus | 2400 | MPa | ISO 178 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |