| Adell Polyamide AF-10-660 is a Polyamide 66 (Nylon 66) material. It is available in North America. Primary attribute of Adell Polyamide AF-10-660: Flame Retardant.&& |
| Product Description | |
|---|---|
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Flame Characteristics |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.28 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.90 to 1.2 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 1.0 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 64.1 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 10 | % | ASTM D638 |
| Bending modulus | 2620 | MPa | ASTM D790 |
| bending strength | |||
| yield | 110 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 43 | J/m | ASTM D256 |
| Tensile impact strength | 137 | kJ/m² | ASTM D1822 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 193 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 76.7 | ℃ | ASTM D648 |
| Melting temperature | 249 to 260 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | 7.7E-5 | 1/℃ | ASTM D696 |
| Relative temperature index | |||
| Electrical performance, 1.50 mm | 65.0 | ℃ | UL 746 |
| Impact mechanical performance, 1.50 mm | 65.0 | ℃ | UL 746 |
| 1.50 mm | 65.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Arc resistance | 104 | sec | ASTM D495 |
| High Arc Burning Index (HAI) | 200 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | 12.7 | mm/min | UL 746 |
| Hot wire ignition | |||
| HWI | 8.0 | sec | UL 746 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |