| Adflex C 200 F is developed for the central layer of tough, transparent co-extruded cast-film structures. It combines transparency with high softness , a very high toughness even at low temperatures and an excellent compatibility with other polyolefins. It does not contain any slip nor anti-blocking agents. Typical applications of the Adflex C 200 F are co-extruded cast-film for food packaging, hygiene applications, surface protection where the outside layer can be any polyolefin homo or copolymer. For regulatory information please refer to Adflex C 200 F Product Stewardship Bulletin (PSB).&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | 聚烯烃，共挤薄膜用聚烯烃 |
| Material Status | Commercial: Active |
| Features | Good Clarity,Good flexibility,Low temperature toughness,Soft |
| Availabilitys | Africa & Middle East ,Latin America,Asia Pacific,Europe |
| Process Methods | Thermo forming |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.890 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 230℃，2.16kg | 6.0 | g/10min | ISO 1133 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| Tensile modulus | ISO 527-3/25 | ||
| MD, 50 µ m, cast thin film | 125 | MPa | ISO 527-3/25 |
| TD, 50 µ m, cast thin film | 110 | MPa | ISO 527-3/25 |
| tensile strength | ISO 527-3/500 | ||
| yield | 8.00 | MPa | ISO 527-2 |
| MD, yield, 50 µ m, blow molded film | 8.00 | MPa | ISO 527-3/500 |
| TD, yield, 50 µ m, blow molded film | 8.00 | MPa | ISO 527-3/500 |
| MD, fracture, 50 µ m, blow molded film | 30.0 | MPa | ISO 527-3/500 |
| TD, fracture, 50 µ m, blow molded film | 24.0 | MPa | ISO 527-3/500 |
| Tensile strain | ISO 527-3/500 | ||
| fracture | 500 | % | ISO 527-2 |
| MD, yield, 50 µ m, cast thin film | 26 | % | ISO 527-3/500 |
| TD, yield, 50 µ m, cast thin film | 33 | % | ISO 527-3/500 |
| MD, fracture, 50 µ m, cast thin film | 990 | % | ISO 527-3/500 |
| TD, fracture, 50 µ m, cast thin film | 890 | % | ISO 527-3/500 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -20℃ | 65 | kJ/m² | ISO 180-1A |
| 23℃ | 无断裂 | ISO 180/1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 50.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| A50 | 89.0 | ℃ | ISO 306/A50 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 50.0 µ m, cast thin film | 47 | ASTM D2457 | |
| Haze | |||
| 50 µ m, cast thin film | 8.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 41 | ISO 868 | |
| Bending modulus | 220 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |