Adflex KS084P - SOLIAO

About
Adflex KS 084 P is a reactor TPO (thermoplastic polyolefin) manufactured using LyondellBasell’s proprietary Catalloy process technology. Adflex KS 084 P features a high melt flow and a low modulus. It is selected by customers for many commercial and industrial extrusion applications. Without exception, all potential activities for applications in the pharmaceutical, medical device, laboratory and diagnostics area have to be discussed with the relevant LyondellBasell Technical and Business contacts first.&&

About

Adflex KS 084 P is a reactor TPO (thermoplastic polyolefin) manufactured using LyondellBasell’s proprietary Catalloy process technology. Adflex KS 084 P features a high melt flow and a low modulus. It is selected by customers for many commercial and industrial extrusion applications. Without exception, all potential activities for applications in the pharmaceutical, medical device, laboratory and diagnostics area have to be discussed with the relevant LyondellBasell Technical and Business contacts first.&&

Product Description
Supplier	LyondellBasell
Generic	聚烯烃，共挤薄膜用聚烯烃
Material Status	Commercial: Active
Features	Good Rigidity,Good flexibility,High impact resistance,High liquidity,Solvent resistance,Puncture Resistant,High ESCR,Low temperature heat sealing
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.890	g/cm³	ISO 1183/A
Melt Flow Rate
230℃，2.16kg	30	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
Shore hardness			ISO 868
Shore D, 15 seconds	35		ASTM D2240
Shore A, 15 seconds	90		ISO 868
Shore D, 15 seconds	35		ISO 868
tensile strength
fracture	7.50	MPa	ISO 527-2
yield	6.00	MPa	ISO 527-2
Tensile strain
fracture	> 800	%	ISO 527-2
Bending modulus	100	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch			ISO 180/1A
-40℃	3.0	kJ/m²	ISO 180-1A
23℃	No Break		ISO 180/1A

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	40.0	℃	ISO 75-2/B
Toughness/brittle transition temperature	-55.0	℃	ISO 6603-2
Vicat Softening Temp
A50	53.0	℃	ISO 306/A50
Melting temperature	164	℃	DSC

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.