| About |
|---|
| Adflex Q 401 F is a reactor TPO (thermoplastic polyolefin) manufactured using LyondellBasell’s proprietary Catalloy process technology. It is suitable for air quenched blown film applications. It contains slip and anti-block additives.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | 聚烯烃，共挤薄膜用聚烯烃 |
| Material Status | Commercial: Active |
| Features | Smoothness,High anti-blocking,High Heat Resistance,Good tear strength,Puncture Resistant |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.890 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 230℃，2.16kg | 0.65 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 49 | ISO 868 | |
| Shore D, 15 seconds | 49 | ASTM D2240 | |
| Bending modulus | |||
| 23℃ | 480 | MPa | ISO 178 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| Secant modulus | |||
| TD, 50 µ m, blow molded film | 300 | MPa | ASTM D882 |
| MD, 50 µ m, blow molded film | 330 | MPa | ASTM D882 |
| tensile strength | |||
| Fracture, 23 ℃ | 21.0 | MPa | ISO 527-2 |
| Yield, 23 ℃ | 15.0 | MPa | ISO 527-2 |
| TD, fracture, 50 µ m, blow molded film | 48.0 | MPa | ASTM D882 |
| TD, yield, 50 µ m, blow molded film | 15.0 | MPa | ASTM D882 |
| MD, fracture, 50 µ m, blow molded film | 68.0 | MPa | ASTM D882 |
| MD, yield, 50 µ m, blow molded film | 18.0 | MPa | ASTM D882 |
| Tensile strain | |||
| Fracture, 23 ℃ | > 800 | % | ISO 527-2 |
| Yield, 23 ℃ | 27 | % | ISO 527-2 |
| TD, fracture, 50 µ m, blow molded film | 870 | % | ASTM D882 |
| MD, fracture, 50 µ m, blow molded film | 670 | % | ASTM D882 |
| Drop hammer impact | |||
| 50 µ m, blow molded film | 550 | g | ISO 7765-1 |
| Elmandorf tear strength | ISO 6383-2 | ||
| MD: 50 µ m, blow molded film | 0.045 | N | ISO 6383-2 |
| TD: 50 µ m, blow molded film | 0.094 | N | ISO 6383-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -40℃ | 4.0 | kJ/m² | ISO 180-1A |
| 23℃ | 60 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 57.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| A50 | 108 | ℃ | ISO 306/A50 |
| Melting temperature | 164 | ℃ | DSC |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Heat resistance | 152 | ℃ | Internal Method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |