Adflex V 109 F

About
Adflex V 109 F is a reactor TPO (thermoplastic polyolefin) manufactured using LyondellBasell’s proprietary Catalloy process technology. It is primarily used for molding, impact modification, extrusion coating and film applications. This resin can be used on conventional injection molding or extrusion equipment. Adflex V 109 F features a very high softness and low modulus, with a relatively high melt flow. The grade is available in natural pellet form.&&

About

Adflex V 109 F is a reactor TPO (thermoplastic polyolefin) manufactured using LyondellBasell’s proprietary Catalloy process technology. It is primarily used for molding, impact modification, extrusion coating and film applications. This resin can be used on conventional injection molding or extrusion equipment. Adflex V 109 F features a very high softness and low modulus, with a relatively high melt flow. The grade is available in natural pellet form.&&

Product Description
Supplier	LyondellBasell
Generic	聚烯烃，共挤薄膜用聚烯烃
Material Status	Commercial: Active
Features	Good Clarity,High liquidity,Soft,low-temperature impact resistance
Availabilitys	North America
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.890	g/cm³	ISO 1183/A
Melt Flow Rate
230℃，2.16kg	12	g/10min	ISO 1133
Shrinkage rate
3.2 mm，48 hrs	0.90	%	ISO 294-4

elastic body	Nominal value	Unit	Test method
tear strength	65.0	kN/m	ASTM D624

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch			ISO 180/1A
-40℃	2.0	kJ/m²	ISO 180-1A
23℃	无断裂		ISO 180/1A

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	35.0	℃	ISO 75-2/B
Toughness/brittle transition temperature	-55.0	℃	ISO 6603-2
Vicat Softening Temp
A50	55.0	℃	ISO 306/A50
Melting temperature	142	℃	ISO 11357-3

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shore D, 15 seconds	30		ASTM D2240 , ISO 868
Shore A, 15 seconds	85		ISO 868
tensile strength			ISO 527-2
yield	5.00	MPa	ISO 527-2
fracture	8.00	MPa	ISO 527-2
Tensile strain			ISO 527-2
yield	> 40	%	ISO 527-2
fracture	> 800	%	ISO 527-2
Bending modulus	80.0	MPa	ISO 178

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.