Adflex X 101 H

About
Adflex X 101 H is a reactor TPO (thermoplastic polyolefin) manufactured using the LyondellBasell’s proprietary Catalloy process technology. It exhibits a high softness and a low modulus, with a relatively high melt flow index. Adflex X 101 H is tailored to replace atactic polypropylene copolymers (APP) used for the modification of bitumen in roofing membranes. The percentage to be added can vary according to the quantity of the atactic polypropylene used in combination with Adflex X 101 H and the requested cold bending temperature of the end product. Due to the high molecular weight of Adflex X 101 H, high blend viscosity and good penetration values are obtained. Its structure is tailored to obtain easy dispersion and phase inversion in the bitumen blend. Adflex X101H is also used in other industrial applications where high flexibility and the capability of accepting high filler loading levels are required. The grade is available in natural pellet form. For regulatory compliance information see Adflex X 101 H Product Stewardship Bulletin (PSB).&&

About

Adflex X 101 H is a reactor TPO (thermoplastic polyolefin) manufactured using the LyondellBasell’s proprietary Catalloy process technology. It exhibits a high softness and a low modulus, with a relatively high melt flow index. Adflex X 101 H is tailored to replace atactic polypropylene copolymers (APP) used for the modification of bitumen in roofing membranes. The percentage to be added can vary according to the quantity of the atactic polypropylene used in combination with Adflex X 101 H and the requested cold bending temperature of the end product. Due to the high molecular weight of Adflex X 101 H, high blend viscosity and good penetration values are obtained. Its structure is tailored to obtain easy dispersion and phase inversion in the bitumen blend. Adflex X101H is also used in other industrial applications where high flexibility and the capability of accepting high filler loading levels are required. The grade is available in natural pellet form. For regulatory compliance information see Adflex X 101 H Product Stewardship Bulletin (PSB).&&

Product Description
Supplier	LyondellBasell
Generic	聚烯烃，共挤薄膜用聚烯烃
Material Status	Commercial: Active
Features	Good flexibility,High liquidity,Solvent resistance,Soft,low-temperature impact resistance,High ESCR
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.880	g/cm³	ISO 1183/A
Melt Flow Rate
230℃，2.16kg	8.0	g/10min	ISO 1133
Shrinkage rate
3.2 mm，48 hrs	1.0	%	ISO 294-4

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shore D, 15 seconds	30		ISO 868
tensile strength
fracture	10.0	MPa	ISO 527-2
yield	6.00	MPa	ISO 527-2
Tensile strain
fracture	> 800	%	ISO 527-2
yield	> 40	%	ISO 527-2
Bending modulus	80.0	MPa	ISO 178

elastic body	Nominal value	Unit	Test method
tear strength	67.0	kN/m	ASTM D624

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch			ISO 180/1A
-40℃	2.0	kJ/m²	ISO 180-1A
23℃	No Break		ISO 180/1A

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	36.0	℃	ISO 75-2/B
Vicat Softening Temp
A50	55.0	℃	ISO 306/A50

Notes
1. Typical properties: these are not to be construed as specifications.
2. Die C, 2.0 in/min
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.