| About |
|---|
| Adflex Z 108 S is a reactor TPO (thermoplastic polyolefin) manufactured using the proprietary Catalloy process technology from LyondellBasell. Adflex Z 108 S features a very high softness, a very low flexural modulus and a high melt flow rate. It is used by customers for injection molding, impact modification, extrusion coating, soft compounding, film and fiber applications. It is also selected by customers for the modification of polypropylene homopolymer and random copolymer without altering the transparency. The grade is available in natural pellet form.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | 聚烯烃，共挤薄膜用聚烯烃 |
| Material Status | Commercial: Active |
| Features | High liquidity,Good Tensile Strength,Soft,low-temperature impact resistance |
| Availabilitys | North America,Latin America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.890 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 230℃，2.16kg | 27 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ISO 868 | ||
| Shore A, 15 seconds | 85 | ISO 868 | |
| Shore D, 15 seconds | 30 | ISO 868 | |
| tensile strength | |||
| fracture | 6.00 | MPa | ISO 527-2 |
| yield | 5.00 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | > 800 | % | ISO 527-2 |
| yield | 20 | % | ISO 527-2 |
| Bending modulus | 80.0 | MPa | ISO 178 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | 62.0 | kN/m | ASTM D624 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -40℃ | 2.0 | kJ/m² | ISO 180-1A |
| 23℃ | No Break | ISO 180/1A | |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| -40℃，3.20 mm，Energy at Peak Load，Ductile Failure | 18.0 | J | ASTM D3763 |
| 23℃，3.20 mm，Energy at Peak Load，Ductile Failure | 10.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 37.0 | ℃ | ISO 75-2/B |
| Toughness/brittle transition temperature | -55.0 | ℃ | ISO 6603-2 |
| Vicat Softening Temp | |||
| A50 | 53.0 | ℃ | ISO 306/A50 |
| Melting temperature | 142 | ℃ | ISO 11357-3 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60 °, 3200 µ m, injection molding | 66 | ASTM D2457 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 7.22 ft/sec |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |