Adflex Z108SE - SOLIAO

About
Adflex Z 108 SE is a reactor TPO (thermoplastic polyolefin) manufactured using the LyondellBasell’s proprietary Catalloy process technology. Adflex Z 108 SE features a very high softness, a very low flexural modulus and a high melt flow rate. It is used for injection molding, impact modification, extrusion coating, soft compounding, film and fiber applications. It is also ideal for the modification of polypropylene homopolymer and random copolymer without altering the transparency. The grade is available in natural pellet form. For regulatory compliance information see Adflex Z 108 SE Product Stewardship Bulletin (PSB).&&

About

Adflex Z 108 SE is a reactor TPO (thermoplastic polyolefin) manufactured using the LyondellBasell’s proprietary Catalloy process technology. Adflex Z 108 SE features a very high softness, a very low flexural modulus and a high melt flow rate. It is used for injection molding, impact modification, extrusion coating, soft compounding, film and fiber applications. It is also ideal for the modification of polypropylene homopolymer and random copolymer without altering the transparency. The grade is available in natural pellet form. For regulatory compliance information see Adflex Z 108 SE Product Stewardship Bulletin (PSB).&&

Product Description
Supplier	LyondellBasell
Generic	聚烯烃，共挤薄膜用聚烯烃
Material Status	Commercial: Active
Features	High liquidity,Good Tensile Strength,Soft,low-temperature impact resistance
Availabilitys	Africa & Middle East ,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Melt Flow Rate
230℃，2.16kg	27	g/10min	ISO 1133

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179
-40℃	2.0	kJ/m²	ISO 179
-20℃	13	kJ/m²	ISO 179
23℃	59	kJ/m²	ISO 179

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	42.8	℃	ISO 75-2/B
Vicat Softening Temp
A50	72.8	℃	ISO 306/A50

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	36		ASTM D2240
Shore D, 15 seconds	36		ISO 868
tensile strength			ISO 527-2
yield	7.80	MPa	ISO 527-2
fracture	15.8	MPa	ISO 527-2
Tensile strain			ISO 527-2
yield	28	%	ISO 527-2
fracture	1100	%	ISO 527-2
Bending modulus	170	MPa	ISO 178

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.