| ADMER™ AT2490E is a maleic anhydride grafted grade based on PE-LLD. It is dedicated to be used as a coupling agent. Added to base polymer it improves the mechanical properties of flame-retarded wire & cable compounds, glass fiber compound and especially wood plastic compounds (WPC).&& |
| Product Description | |
|---|---|
| Supplier | Mitsui |
| Generic | MAH-g-PE增容剂 |
| Material Status | Commercial: Active |
| Features | Food contact compliance,Low density |
| Availabilitys | Africa & Middle East ,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.923 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.40 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | 无断裂 | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 98.0 | ℃ | ASTM D1525 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 50 | ASTM D2240 | |
| Tensile modulus | 43.0 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 31.0 | MPa | ASTM D638 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. wood plastic compounds (WPC) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |