| About |
|---|
| ADMER® QF551E is a maleic anhydride grafted, co-PP based grade for strong bonding between PP and EVOH, PA or Aluminum, and is therefore suitable for high performance applications in blown film, composite pipe, injection molding or coating process.&& |
| Product Description | |
|---|---|
| Supplier | Mitsui |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Food contact compliance |
| Availabilitys | Africa & Middle East ,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.890 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 5.0 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | 无断裂 | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 120 | ℃ | ASTM D1525 |
| Melting peak temperature | 147 | ℃ | ASTM D3418 |
| Oxygen sensing time | |||
| 210℃ | 7.0 | min | ISO 11357-6 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 59 | ASTM D2240 | |
| tensile strength | ASTM D638 | ||
| yield | 17.0 | MPa | ASTM D638 |
| fracture | 17.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 500 | % | ASTM D638 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |