| About |
|---|
| AdSint® PA11 black is a bio-based material made from castor oil. The end product offers a high elongation at break, elasticity and high impact resistance. Typical applications are in environments with high mechanical stress (e.g. hinges) and special surroundings (e.g. chemical, detergents, oil). Due to its high ductility, it does not splinter in crash situations. AdSint® PA11 black has been tested on most common SLS printers. Parameters for printing will be provided. It is also available in nature and white. The refresh rate is between 35% – 50%, depending on the application.&& |
| Product Description | |
|---|---|
| Generic | PA 11 |
| Material Status | Commercial: Active |
| Features | High impact resistance,Ductility,High elastic,Renewable resources,Good Tensile Strength |
| Availabilitys | Europe |
| Process Methods | 3D Printing, Laser Sintering/Melting |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.00 to 1.10 | g/cm³ | ISO 61 |
| Apparent density | 0.61 to 0.71 | g/cm³ | ISO 1068 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.90 to 1.1 | % | ISO 62 |
| Particle size distribution | |||
| Course Particles <15 µm | < 10 | % | |
| Course Particles >76 µm | < 10 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 100 to 160 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 148 to 152 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 53.0 to 57.0 | ℃ | ISO 75-2/A |
| Glass transition temperature | 39.0 to 43.0 | ℃ | ISO 11357-2 |
| Melting temperature | |||
| — | 188 to 192 | ℃ | |
| — | 199 to 203 | ℃ |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Mean Diameter | 40.0 | µm | ISO 13320 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 20 ℃ | 75 to 77 | ISO 868 | |
| Tensile modulus | 1530 to 1830 | MPa | ISO 527-2/1B |
| tensile strength | |||
| fracture | 45.0 to 49.0 | MPa | ISO 527-2/1B |
| Tensile strain | |||
| fracture | 34 to 40 | % | ISO 527-2/1B |
| Bending modulus | |||
| 23℃ | 1250 to 1550 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Packed |
| 3. Sintered Part |
| 4. Part |
| 5. Powder |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |