| Adstif HA612M is a high crystallinity polypropylene homopolymer with an extremely high stiffness, good transparency and outstanding high temperature performances. It is especially designed for cast film applications where high rigidity, transparency and very good thermal characteristics are required. Adstif HA612M is particularly recommended for the production of coex film for Twist Wrapping on high speed packaging lines. Other applications include flowers and textile packaging, sterilizable and pasteurizable food packaging. Adstif HA612M does not contain neither slip nor antiblocking agents and is suitable for metallisable films. It is Calcium Stearate free. For regulatory information please refer to Adstif HA612M Product Stewardship Bulletin (PSB).&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | HC PP |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Clarity,Crystal,Homopolymer |
| Availabilitys | Africa & Middle East ,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 7.0 | g/10min | ISO 1133 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| Secant modulus | |||
| MD, 50 µ m, cast thin film | 900 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield, 50 µ m, extruded film | 22.0 | MPa | ASTM D882 |
| MD, fracture, 50 µ m, extruded film | 37.0 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, yield, 50 µ m, extruded film | 7.0 | % | ASTM D882 |
| MD, fracture, extruded film | 860 | % | ASTM D882 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 106 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| A50 | 158 | ℃ | ISO 306/A50 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 50.0 µ m, cast thin film | 69 | ASTM D2457 | |
| Haze | |||
| 50 µ m, cast thin film | 5.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 72 | ISO 868 | |
| Tensile modulus | 1900 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 38.0 | MPa | ISO 527-2/50 |
| Tensile strain | ISO 527-2 | ||
| yield | 7.0 | % | ISO 527-2 |
| fracture | 20 | % | ISO 527-2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.98 in/min |
| 3. 20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |