| About |
|---|
| Adsyl 7416 XCP is an advanced polyolefin selected by customers for use as a sealing layer in coextruded film applications. This grade features a low seal initiation temperature and good optics. It does not contain slip or anti-block additives.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | 聚烯烃，共挤薄膜用聚烯烃 |
| Material Status | Commercial: Active |
| Features | Optical performance,Low temperature heat sealing |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 230℃，2.16kg | 7.5 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Bending modulus | 600 | MPa | ISO 178 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| Tensile modulus | ISO 527-3/25 | ||
| MD，50 µm | 290 | MPa | ISO 527-3/25 |
| TD, 50 µ m, cast thin film | 320 | MPa | ISO 527-3/25 |
| tensile strength | ISO 527-3/500 | ||
| yield | 21.0 | MPa | ISO 527-2 |
| MD, yield, 50 µ m, blow molded film | 15.0 | MPa | ISO 527-3/500 |
| TD, yield, 50 µ m, blow molded film | 15.0 | MPa | ISO 527-3/500 |
| tensile strength | ISO 527-3/500 | ||
| MD, fracture, 50 µ m, blow molded film | 40.0 | MPa | ISO 527-3/500 |
| TD, fracture, 50 µ m, blow molded film | 42.0 | MPa | ISO 527-3/500 |
| Tensile strain | ISO 527-3/500 | ||
| yield | 14 | % | ISO 527-2 |
| MD, fracture, 50 µ m, cast thin film | 950 | % | ISO 527-3/500 |
| TD, fracture, 50 µ m, cast thin film | 900 | % | ISO 527-3/500 |
| Tensile strain | ISO 527-3/500 | ||
| MD, yield, 50 µ m, cast thin film | 19 | % | ISO 527-3/500 |
| TD, yield, 50 µ m, cast thin film | 12 | % | ISO 527-3/500 |
| Initial sealing temperature | 115 | ℃ | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 65.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| A50 | 115 | ℃ | ISO 306/A50 |
| Melting temperature | 133 | ℃ | ISO 11357-3 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 50.0 µ m, cast thin film | 90 | ASTM D2457 | |
| Haze | |||
| 50 µ m, cast thin film | 0.50 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |