Advanced-PP 1102LQ

About
Advanced-PP 1102LQ is a propylene homopolymer with narrow MFR and with very low water carry over properties. It is specificially designed for stretched tape yarn, carpet backing and artificial grass. Also suited for Raffia & Thermoforming Applications. Application Thermoformed Parts, Raffia, Carpet backing & General Extrusion. Regulatory Information: The Grade Advanced-PP 1102LQ and additives incorporated comply with United States FDA Regulation 21CFR 177.1520 Olefin Polymers and European Regulation (EU) 10/2011. Specific information is available upon request.&&

About

Advanced-PP 1102LQ is a propylene homopolymer with narrow MFR and with very low water carry over properties. It is specificially designed for stretched tape yarn, carpet backing and artificial grass. Also suited for Raffia & Thermoforming Applications. Application Thermoformed Parts, Raffia, Carpet backing & General Extrusion. Regulatory Information: The Grade Advanced-PP 1102LQ and additives incorporated comply with United States FDA Regulation 21CFR 177.1520 Olefin Polymers and European Regulation (EU) 10/2011. Specific information is available upon request.&&

Product Description
Generic	PP homopolymerization
Material Status	Commercial: Active
Features	Homopolymer
Availabilitys	Africa & Middle East ,Asia Pacific
Process Methods	Thermo forming

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.910	g/cm³	ISO 1183
Melt Flow Rate
230℃，2.16kg	4.5	g/10min	ISO 1133

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23℃	3.5	kJ/m²	ISO 179/1eA
Charpy Unnotch Impact strength
23℃	140	kJ/m²	ISO 179/1eU
Impact strength of cantilever beam notch
23℃	3.5	kJ/m²	ISO 180-1A

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	85.0	℃	ISO 75-2/B
Vicat Softening Temp
A50	154	℃	ISO 306/A50
Melting temperature
DSC	163	℃	ISO 3146

MECHANICAL	Nominal value	Unit	Test method
Ball hardness
H358/30	74.0	MPa	ISO 2039-1
Tensile modulus	1500	MPa	ISO 527-1-2
tensile strength
yield	34.0	MPa	ISO 527-2/50
Tensile strain			ISO 527-2/50
yield	9.0	%
fracture	> 50	%

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.