| ADVANCENE™ EM-2420-AAB Linear Low Density Polyethylene (LLDPE) Resin is produced using advanced gas phase PE process and is intended for use in general purpose injection molding applications. This resin has been designed to have excellent impact strength, rigidity, environmental stress crack resistance and processability. Main Charactelistics : Injection molding. General purpose applications. Excellent low temperature impact strength, rigidity, stress crack resistance and processability. Very narrow molecular weight distribution.&& |
| Product Description | |
|---|---|
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,High impact resistance,Weight distribution,Low density,low-temperature impact resistance,High ESCR |
| Availabilitys | Africa & Middle East ,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.924 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 20 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 50 ℃, 100% non-ionic surfactant, F50 | 20.0 | hr | ASTM D1693 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile impact strength | |||
| — | 168 | kJ/m² | ASTM D1822 |
| — | 168 | kJ/m² | ISO 8256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 42.8 | ℃ | ASTM D648 |
| Embrittlement temperature | < -76.1 | ℃ | ASTM D746 |
| Vicat Softening Temp | 93.9 | ℃ | ASTM D1525 |
| Melting peak temperature | 123 | ℃ | ASTM D3418 |
| Crystallization peak temperature | |||
| DSC | 108 | ℃ | ASTM D3418 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 50 | ASTM D2240 | |
| tensile strength | |||
| yield | 11.7 | MPa | |
| fracture | 7.60 | MPa | |
| Tensile strain | |||
| yield | 3.0 | % | |
| fracture | 60 | % | |
| Bending modulus | |||
| 2% secant | 386 | MPa | ASTM D790-B |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type S |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |