| About |
|---|
| ADVANCENE™ EM-4925-AAH HDPE Resin is specifically designed for use in either intermittent or continuous blow molding equipment to produce containers up to 30 liters in size – applications that require the combination of outstanding environmental stress crack resistance (ESCR) and high impact strength. ADVANCENE™ EM-4925-AAH HDPE Resin is also considered a multipurpose blow molding resin designed for the high speed production of blow molded containers used for packaging household industrial chemicals (e.g. detergents, bleach, fabric softeners), toiletries and cosmetics (e.g., shampoos, creams, lotions, etc.) health and medical aids. In addition, it can be blow molded into other thin-walled parts and houseware items, and can also be extruded into profiles or sheets. Main Characteristics Outstanding environmental stress crack resistance. High impact strength. Good extrusion characteristics.&& |
| Product Description | |
|---|---|
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | High impact resistance,High density,High ESCR |
| Availabilitys | Africa & Middle East ,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.949 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.25 | g/10min | |
| 190℃，21.6kg | 25 | g/10min | |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 50 ℃, 100% non-ionic surfactant, F50 | 180 | hr | ASTM D1693 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile impact strength | |||
| — | 210 | kJ/m² | ASTM D1822 |
| — | 210 | kJ/m² | ISO 8256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 62.0 | ℃ | ASTM D648 |
| Embrittlement temperature | < -76.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 127 | ℃ | ASTM D1525 |
| Melting peak temperature | 130 | ℃ | ASTM D3418 |
| Crystallization peak temperature | |||
| DSC | 118 | ℃ | ASTM D3418 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 57 | ASTM D2240 | |
| tensile strength | |||
| yield | 23.4 | MPa | |
| fracture | 31.0 | MPa | |
| Tensile strain | |||
| yield | 8.0 | % | |
| fracture | 900 | % | |
| Bending modulus | |||
| 2% secant | 910 | MPa | ASTM D790-B |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type S |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |