| ADVANCENE™ EM-5333-AAH HDPE Resin is a multipurpose polymer designed for high speed production of blow molded containers used to package household industrial chemicals (e.g detergents, bleach, fabric softeners), toiletries and cosmetics (e.g shampoos, creams, lotions, etc.), health and medical aids, and food products. In addition, it can be blow molded into other thin-walled parts and houseware items, and can be extruded into profiles. Main Characteristics: Excellent environmental stress crack resistance and rigidity. High impact strength. Moderate swell. High melt strength.&& |
| Product Description | |
|---|---|
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | High impact resistance,Good melt strength,High density,High ESCR |
| Availabilitys | Africa & Middle East ,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.953 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.38 | g/10min | |
| 190℃，21.6kg | 33 | g/10min | |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 50 ℃, 100% non-ionic surfactant, F50 | 80.0 | hr | ASTM D1693 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile impact strength | |||
| — | 168 | kJ/m² | ASTM D1822 |
| — | 168 | kJ/m² | ISO 8256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 73.0 | ℃ | ASTM D648 |
| Embrittlement temperature | < -76.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 129 | ℃ | ASTM D1525 |
| Melting peak temperature | 131 | ℃ | ASTM D3418 |
| Crystallization peak temperature | |||
| DSC | 118 | ℃ | ASTM D3418 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 61 | ASTM D2240 | |
| tensile strength | |||
| yield | 26.9 | MPa | |
| fracture | 31.0 | MPa | |
| Tensile strain | |||
| yield | 7.0 | % | |
| fracture | 1000 | % | |
| Bending modulus | |||
| 2% secant | 1000 | MPa | ASTM D790-B |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type S |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |