| Low-smoke, low-toxicity, halogen-free, flame-retardant, silane crosslinkable compound for low voltage insulation and sheathing of all types of cable This is a low smoke, low fume, fire retardant silane crosslinkable compound which can be processed as a thermoplastic at high output rates and cured post processing by exposure to moisture. The graft component SX538 is mixed with a crosslinking catalyst masterbatch CM540U generally in the ratio 95:5. The compound combines good mechanical, electrical and fire retardant properties to meet demanding insulation specifications including BS7211. The compound can also be used for sheathing of cables requiring high fire retardancy.&& |
| Product Description | |
|---|---|
| Generic | XLPE |
| Material Status | Commercial: Active |
| Features | Low smoke,Crosslinked,Halogen free,Flame Characteristics,Low toxicity,Low odor |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.51 | g/cm³ | BS 2782 620A |
| Melt Flow Rate | |||
| 190℃，2.16kg | 7.5 | g/10min | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 14.0 | MPa | IEC 60811-1-1 |
| Tensile strain | |||
| fracture | 150 | % | IEC 60811-1-1 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength | |||
| 70 ℃, 72 hr, in ASTM # 2 oil | -47 | % | |
| 100 ℃, 24 hours, in ASTM # 2 oil | -58 | % | |
| 135℃，168 hr | 20 | % | IEC 60811-1-2 |
| Changes in tensile stress during fracture | |||
| 70 ℃, 72 hr, in ASTM # 2 oil | 3.0 | % | |
| 100 ℃, 24 hours, in ASTM # 2 oil | -20 | % | |
| 135℃，168 hr | -15 | % | IEC 60811-1-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Low temperature bending | |||
| -30℃ | pass | IEC 60811-1-4 | |
| thermosetting | IEC 60811-2-1 | ||
| Elongation under load: 20 N/cm ²， 200 ℃ | 30 | % | IEC 60811-2-1 |
| Maximum permanent elongation after cooling | 0.0 | % | IEC 60811-2-1 |
| Temperature index | > 300 | ℃ | ISO 4589-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Insulation resistance constant – Ki | IEC 60502 | ||
| 20℃ | 1.3E+12 | ohms·cm | IEC 60502 |
| 90℃ | 2.9E+8 | ohms·cm | IEC 60502 |
| Conductivity | |||
| of gases | 13.0 | µS/cm | IEC 60754-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Extreme oxygen index | 36 | % | ISO 4589-2 |
| Corrosive gases in flue gas | |||
| pH | 4.60 | IEC 60754-2 | |
| Smoke density | < 3.5 | % | ASTM D2843 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Halogen Acid Gas Evolution | < 0.50 | % | IEC 60754-1 |
| Hot pressing test | |||
| 100℃ | 40 | % | IEC 60811-2-1 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 130 | °C | |
| Barrel 2 zone temperature | 150 | °C | |
| Barrel 3 zone temperature | 170 | °C | |
| Barrel 4 zone temperature | 180 | °C | |
| Head temperature | 190 | °C | |
| Nozzle temperature | 190 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |