AEI SX545:CM540U

About
Low smoke, low-toxicity, halogen-free, flame-retardant, silane crosslinkable compound for insulation of LV cables and sheathing of all types of cables This is a low smoke, low fume, fire retardant silane crosslinkable compound, which can be processed like a thermoplastic material at high output rates. The graft component SX545 is mixed with the crosslinking catalyst CM540U generally in the ratio 95:5. The compound combines good mechanical, electrical and fire retardant properties to meet demanding insulation specifications such as BS7211. This compound can also be used for sheathing of cables which require high levels of fire retardancy.&&

About

Low smoke, low-toxicity, halogen-free, flame-retardant, silane crosslinkable compound for insulation of LV cables and sheathing of all types of cables This is a low smoke, low fume, fire retardant silane crosslinkable compound, which can be processed like a thermoplastic material at high output rates. The graft component SX545 is mixed with the crosslinking catalyst CM540U generally in the ratio 95:5. The compound combines good mechanical, electrical and fire retardant properties to meet demanding insulation specifications such as BS7211. This compound can also be used for sheathing of cables which require high levels of fire retardancy.&&

Product Description
Generic	XLPE
Material Status	Commercial: Active
Features	Low smoke,Crosslinked,Halogen free,Flame Characteristics,Low toxicity,Low odor
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.49	g/cm³	BS 2782 620A

MECHANICAL	Nominal value	Unit	Test method
tensile strength	12.0	MPa	IEC 60811-1-1
Tensile strain
fracture	140	%	IEC 60811-1-1

Aging performance	Nominal value	Unit	Test method
The rate of change in tensile strength
135℃，168 hr	20	%	IEC 60811-1-2
Changes in tensile stress during fracture
135℃，168 hr	-15	%	IEC 60811-1-2

THERMAL	Nominal value	Unit	Test method
deformation
K=1，100℃	30	%	IEC 60811-3-1
Low temperature bending
-30℃	pass		IEC 60811-1-4
thermosetting			IEC 60811-2-1
Elongation under load: 20 N/cm ²， 200 ℃	50	%	IEC 60811-2-1
Maximum permanent elongation after cooling	0.0	%	IEC 60811-2-1
Temperature index	260	℃	ISO 4589-3

Electrical performance	Nominal value	Unit	Test method
Conductivity
of gases	13.0	µS/cm	IEC 60754-2
Insulation resistance constant
Ki，90℃	0.29	Mohms·km	IEC 60502

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Extreme oxygen index	32	%	ISO 4589-2
Corrosive gases in flue gas
pH	4.60		IEC 60754-2
Smoke density	< 3.5	%	ASTM D2843

Supplementary information	Nominal value	Unit	Test method
Halogen Acid Gas Evolution	< 0.50	%	IEC 60754-1

Process Conditions
Extrusion	Nominal value	Unit	Test method
Barrel 1 zone temperature	130	°C
Barrel 2 zone temperature	140	°C
Barrel 3 zone temperature	145	°C
Barrel 4 zone temperature	150	°C
Head temperature	160	°C
Nozzle temperature	160	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.