AEI SX738:CM424

About
Low-smoke, low-toxicity, halogen-free, flame retardant, silane crosslinkable compound for the production of flexible heat shrinkable tubing. SX738 is a low smoke, low fume, fire retardant silane grafted compound, curable by exposure to moist conditions. This is designed specifically for the production, by extrusion, of flame retardant halogen free heat shrinkable tubing. The graft component SX738 is mixed with a crosslinking catalyst masterbatch CM424 generally in the ratio 95:5. The two component system SX738:CM424 combines ease of processing with the ability to achieve a degree of crosslinking compatible with good expansion and contraction.&&

About

Low-smoke, low-toxicity, halogen-free, flame retardant, silane crosslinkable compound for the production of flexible heat shrinkable tubing. SX738 is a low smoke, low fume, fire retardant silane grafted compound, curable by exposure to moist conditions. This is designed specifically for the production, by extrusion, of flame retardant halogen free heat shrinkable tubing. The graft component SX738 is mixed with a crosslinking catalyst masterbatch CM424 generally in the ratio 95:5. The two component system SX738:CM424 combines ease of processing with the ability to achieve a degree of crosslinking compatible with good expansion and contraction.&&

Product Description
Generic	XLPE
Material Status	Commercial: Active
Features	Excellent Processability,Low smoke,Crosslinked,Halogen free,Flame Characteristics
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.40	g/cm³	BS 2782 620A

MECHANICAL	Nominal value	Unit	Test method
tensile strength	10.0	MPa	IEC 60811-1-1
Tensile strain
fracture	200	%	IEC 60811-1-1

Aging performance	Nominal value	Unit	Test method
The rate of change in tensile strength
135℃，168 hr	< 25	%	IEC 60811-1-2
Changes in tensile stress during fracture
135℃，168 hr	< 25	%	IEC 60811-1-2

THERMAL	Nominal value	Unit	Test method
Temperature index	> 200	℃	ISO 4589-3

Electrical performance	Nominal value	Unit	Test method
Volume resistivity	1.0E+13	ohms·cm	IEC 60502
Dielectric strength	14	kV/mm	IEC 60243-1
Conductivity
of gases	13.0	µS/cm	IEC 60754-2

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Extreme oxygen index	26	%	ISO 4589-2
Corrosive gases in flue gas
pH	4.60		IEC 60754-2
Smoke density	< 3.5	%	ASTM D2843

Supplementary information	Nominal value	Unit	Test method
Halogen Acid Gas Evolution	< 0.50	%	IEC 60754-1
High temperature elongation
35 lb/mm²，150℃	< 180	%	Internal Method

Process Conditions
Extrusion	Nominal value	Unit	Test method
Barrel 1 zone temperature	130	°C
Barrel 2 zone temperature	150	°C
Barrel 3 zone temperature	170	°C
Barrel 4 zone temperature	180	°C
Head temperature	190	°C
Nozzle temperature	190	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.