| About |
|---|
| Compound based on Polyamide 66 (PA 66). Heat stabilised. UL94 V-0 classified, halogens and red phosphorus free. Product UL certified.&& |
| Product Description | |
|---|---|
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Low Halogen Content,Low to no phosphorus content,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.954 | g/cm³ | BS 2782 620A |
| Melt Flow Rate | |||
| 190℃，2.16kg | 4.5 | g/10min | Internal Method |
| ESCR(Environmental Stress Cracking Resistance) | 20.0 | hr | ASTM D1693A |
| Gel content | 62 | % | ASTM D2765 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 1% secant | 900 | MPa | BS 2782 320A |
| tensile strength | 26.0 | MPa | IEC 60811-1-1 |
| Tensile strain | |||
| fracture | 450 | % | IEC 60811-1-1 |
| abrasion resistance | 160 | mm³ | ISO 4649 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180 | ||
| -30℃ | 6.0 | kJ/m² | ISO 180 |
| 23℃ | 12 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| thermosetting | IEC 60811-2-1 | ||
| Elongation under load: 20 N/cm ²， 200 ℃ | 60 | % | IEC 60811-2-1 |
| Maximum permanent elongation after cooling | 5.0 | % | IEC 60811-2-1 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Crosslinking – in hot water | |||
| 95 to 100 ℃, 1.00 mm | 5.0 | hr | |
| 95 to 100 ℃, 2.00 mm | 12.0 | hr | |
| 95 to 100 ℃, 3.00 mm | 24.0 | hr |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |