| About |
|---|
| Thermoplastic, low-smoke, halogen-free flame retardant compound for data and communication cable. This is a flame-retardant low-smoke thermoplastic compound, which has been specially developed to meet the requirements of limited toxic and corrosive fume emission. TP519C has been developed to offer good processability at high extrusion speeds and has very little die drool. TP519C is available in the following versions: TP519C (natural colour) TP519CB (coloured black) TP519CU (with a non-staining UV stabiliser added) TP519CBU (carbon black added to give UV stability)&& |
| Product Description | |
|---|---|
| Generic | PE |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Excellent Processability,Low smoke,Halogen free,Flame Characteristics |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.50 | g/cm³ | BS 2782 620A |
| Melt Flow Rate | |||
| 150℃，21.6kg | 14 | g/10min | Internal Method |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength | |||
| 50℃，336 hr，in Hydrochloric Acid，1N | 17 | % | |
| 50℃，336 hr，in Sodium Hydroxide，1N | 45 | % | |
| 70 ℃, 4 hours, in ASTM # 2 oil | 18 | % | |
| 135℃，168 hr | 12 | % | IEC 60811-1-2 |
| Changes in tensile stress during fracture | |||
| 50℃，336 hr，in Hydrochloric Acid，1N | 14 | % | |
| 50℃，336 hr，in Sodium Hydroxide，1N | 20 | % | |
| 70 ℃, 4 hours, in ASTM # 2 oil | 7.0 | % | |
| 135℃，168 hr | -10 | % | IEC 60811-1-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| deformation | |||
| 80℃ | 15 | % | IEC 60811-3-1 |
| Cold shock | |||
| -30℃ | pass | IEC 60811-1-4 | |
| Low temperature bending | |||
| Temperature index | 270 | ℃ | ISO 4589-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| 20 ℃ | 2.0E+14 | ohms·cm | IEC 60502 |
| Dielectric strength | |||
| 20 ℃ | 19 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 23℃，50 Hz | 4.65 | IEC 60250 | |
| Insulation resistance constant – Ki | IEC 60502 | ||
| 20℃ | 9.5E+10 | ohms·cm | IEC 60502 |
| 90℃ | 6.5E+7 | ohms·cm | IEC 60502 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Extreme oxygen index | 31 | % | ISO 4589-2 |
| smoke | |||
| 3m cube test | pass | EN 61034 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Halogen Acid Gas Evolution | < 0.50 | % | IEC 60754-2 |
| tear strength | 5 | N/mm | BS 6469 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 90 | ||
| tensile strength | 13.0 | MPa | IEC 60811-1-1 |
| Tensile strain | |||
| fracture | 140 | % | IEC 60811-1-1 |
| Fracture, -30 ℃ | 50 | % | IEC 60811-1-4 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 115 | °C | |
| Barrel 2 zone temperature | 125 | °C | |
| Barrel 3 zone temperature | 135 | °C | |
| Barrel 4 zone temperature | 145 | °C | |
| Melt temperature | < 170 | °C | |
| Head temperature | 155 | °C | |
| Nozzle temperature | 160 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |