| About |
|---|
| Excellent inherent cling properties Excellent optical properties Excellent toughness properties Complies with: U.S. FDA FCN 424 Canadian HPFB No Objections Consult the regulations for complete details. AFFINITY* KC 8852G Polyolefin Plastomer (POP) is produced via INSITE* Technology. This resin is an ethyleneoctene copolymer that offers excellent performance as a cling resin in one-sided stretch cling film applications. This polyolefin plastomer provides excellent cling and optics, while offering outstanding toughness.&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | POP |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.875 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 3.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 20 | µm | |
| Membrane puncture resistance | |||
| 20 µm | 15.7 | J/cm³ | Internal Method |
| Drop hammer impact | |||
| 20 µ m, cast thin film | 150 | g | ASTM D1709 |
| Film bonding | Nominal value | Unit | Test method |
|---|---|---|---|
| 20.3 µm | 250 | g | |
| 20.3 µm | 130 | g | |
| 20.3 µm | 150 | g | |
| 20.3 µm | 110 | g |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 48.0 | ℃ | ASTM D1525 |
| Melting temperature | |||
| DSC | 68.0 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 20.3 µ m, cast thin film | 66 | ASTM D2457 | |
| Haze | |||
| 20.3 µ m, cast thin film | 4.3 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Blown Film, Unstretched |
| 3. Blown Film, 200% Stretched |
| 4. Cast Film, Unstretched |
| 5. Cast Film, 200% Stretched |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |