| About |
|---|
| AFFINITY* PL 1840G Polyolefin Plastomer (POP) is produced via INSITE* Technology. It is an ethylene alpha-olefin resin designed to provide blown film with low temperature sealability, good puncture resistance, optics and organoleptic properties. It also has excellent compatibility with other polyolefins, allowing efficient blending and coextrusion. Outstanding low temperature sealability and toughness Suitable as a sealant in liquid & dry food pouch applications Applications: Blown Film Complies with: Canadian HPFP No Objection EU, No 10/2011 U.S. FDA FCN 424 U.S. FDA-DMF Consult the regulations for complete details.&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | POP |
| Material Status | Commercial: Active |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.909 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 51 | µm | |
| Membrane puncture strength | |||
| 51 µm | 9.16 | J | Internal Method |
| Membrane puncture force | |||
| 51 µm | 93.0 | N | Internal Method |
| Membrane puncture resistance | |||
| 51 µm | 25.2 | J/cm³ | Internal Method |
| Secant modulus | ASTM D882 | ||
| 2% secant, MD: 51 µ m | 123 | MPa | ASTM D882 |
| 2% secant, TD: 51 µ m | 123 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield, 51 µ m | 8.76 | MPa | ASTM D882 |
| TD, yield, 51 µ m | 8.07 | MPa | ASTM D882 |
| MD, fracture, 51 µ m | 47.8 | MPa | ASTM D882 |
| TD, fracture, 51 µ m | 45.4 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 51 µ m | 620 | % | ASTM D882 |
| TD, fracture, 51 µ m | 580 | % | ASTM D882 |
| Drop hammer impact | |||
| 51 µm | > 830 | g | ASTM D1709-B |
| Elmandorf tear strength | ASTM D1922 | ||
| MD：51 µm | 560 | g | ASTM D1922 |
| TD：51 µm | 840 | g | ASTM D1922 |
| Initial sealing temperature | |||
| 51 µm | 92.8 | ℃ | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 95.0 | ℃ | ASTM D1525 |
| Melting temperature | |||
| DSC | 106 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 20°，50.8 µm | 128 | ASTM D2457 | |
| transparency | |||
| 50.8 µm | 63.0 | ASTM D1746 | |
| Haze | |||
| 50.8 µm | 2.5 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 221 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Modified rectangular test specimen. |
| 3. Temperature at which 2 lb/in. (8.8 N/25.4 mm) heat seal strength is achieved. Heat Seal Strengths, Topwave HT Tester 0.5 S dwell, 40 psi bar pressure, pull speed 10 in./min (250 mm/sec). |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |