| AIE ABS 2010AF是一种丙烯腈丁二烯苯乙烯(ABS)材料,。 该产品在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货,加工方式为:注射成型。 AIE ABS 2010AF的主要特性有: 阻燃/额定火焰 Flame Retardant&& |
| Product Description | |
|---|---|
| Supplier | Asia International Enterprise (Hong Kong) |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,V-0,5VA |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，3.80kg | 15 | g/10min | ISO 1133 |
| Shrinkage rate | 0.40 to 0.70 | % | Internal Method |
| Water absorption rate | |||
| 23℃，24hr | 0.30 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 44.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 20 | % | ISO 527-2 |
| Bending modulus | 2500 | MPa | ISO 178 |
| bending strength | 70.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 23 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 87.0 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 82.0 | ℃ | ISO 75-2/A |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | 5VA |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |