| About |
|---|
| Materials Features: It is suitable for hot-plate welding. It has high melt flow stregth and high sag resistance. It can be made into products of semi-transparent, low temperature resistance, impact resistance materials for automotive, motorcycle carbon canister housings, automotive expansion tank, accumulator case, power battery cases and other parts that require for hot-plate welding.&& |
| Product Description | |
|---|---|
| Supplier | Asia International Enterprise (Hong Kong) |
| Generic | PP not specified |
| Material Status | Commercial: Negative |
| Features | High impact resistance,High liquidity,Antifreeze,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.910 | g/cm³ | ASTM D792 |
| Shrinkage rate | ASTM D955 | ||
| MD | 1.5 | % | ASTM D955 |
| TD | 1.7 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 23.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 160 | % | ASTM D638 |
| Bending modulus | 700 | MPa | ASTM D790 |
| bending strength | 27.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | 500 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 74.0 | ℃ | ASTM D648 |
| Melting temperature | 170 | ℃ | DSC |
| Linear coefficient of thermal expansion | |||
| MD：-20~150℃ | 5.5E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| 23℃ | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric constant | |||
| 1 MHz | 3.10 | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 23°C |
| 3. 2.0 in/min |
| 4. 0.12 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |