| AIE PPO 9010-G30是一种聚苯醚 + PS (PPE+PS)材料,含有的填充物为30% 玻璃纤维增强材料。 该产品在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货,加工方式为:注射成型。 AIE PPO 9010-G30的主要特性为:阻燃/额定火焰。&& |
| Product Description | |
|---|---|
| Supplier | Asia International Enterprise (Hong Kong) |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.30 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 280℃，5.0kg | 3.0 | g/10min | ISO 1133 |
| Shrinkage rate | 0.20 to 0.50 | % | ISO 2577 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 112 | MPa | ISO 527-2/1/50 |
| Bending modulus | 7000 | MPa | ISO 178 |
| bending strength | 150 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 12 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 158 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed, 3.2 mm span | 138 | ℃ | ISO 75-2/A |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+17 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 to 110 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Processing (melt) temperature | 240 to 300 | °C | |
| Mold temperature | 70.0 to 100 | °C | |
| Injection pressure | 30.0 to 80.0 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |