| About |
|---|
| Solef® 9009 PVDF homopolymer is a semi-crysalline fluoropolymer. Solef® film is chemically inert to most acids, aliphatic and aromatic organic compounds, chlorinated solvents and alcohols. Solef® PVDF flim has a very high purity, abrasion resistance comparable to that of polyamides and relatively low coefficient of friction. These films can be used in a wide range of temperatures and have excellent intrinsic fire resistance. Solef® PVDF films have demonstrated excellent weathering properties and are extremely resistant to UV radiation and common industrial and environmental pollutants. Solef® PVDF films can be used in a wide range of applications, including release films, filters, chemical resistance lining, outdoor UV resistant needs as well as electric and electronic applications.&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PVDF |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Homopolymer |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.75 to 1.80 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| 23℃，24hr | < 0.040 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | ASTM D1894 | ||
| With oneself – dynamic | 0.15 to 0.35 | ||
| With oneself – static | 0.20 to 0.40 | ||
| Taber abraser | |||
| 1000 cycles, 1000 g, CS-10 wheels | 5.00 to 10.0 | mg | ASTM D4060 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| Secant modulus | ASTM D882 | ||
| MD | 2000 | MPa | |
| TD | 2100 | MPa | |
| tensile strength | ASTM D882 | ||
| MD, yield | 55.0 | MPa | |
| TD, yield | 56.0 | MPa | |
| MD, fracture | 57.0 | MPa | |
| TD, fracture | 54.0 | MPa | |
| Tensile strain | ASTM D882 | ||
| MD, yield | 6.0 | % | |
| TD, yield | 6.2 | % | |
| MD, fracture | 200 | % | |
| TD, fracture | 250 | % | |
| Free contraction | |||
| 130℃ | 0.70 | % | ASTM D2732 |
| Area coefficient | 108 | ft²/lb/mil |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | -40.0 | ℃ | ASTM D4065 |
| Melting temperature | 162 to 168 | ℃ | ASTM D3418 |
| Crystallization peak temperature | |||
| DSC | 133 to 140 | ℃ | ASTM D3418 |
| Linear coefficient of thermal expansion | |||
| MD | 1.4E-4 | 1/℃ | ASTM D696 |
| specific heat | |||
| 100℃ | 1600 | J/kg/℃ | ASTM C351 |
| Thermal conductivity coefficient | 0.20 | W/m/K | ASTM C177 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+14 | ohms | ASTM D257 |
| Volume resistivity | > 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 23 ℃，1 mm | 20 to 25 | kV/mm | ASTM D149 |
| Dielectric constant | 7.50 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Extreme oxygen index | |||
| 3.0 mm | 44 | % | ASTM D2863 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |