Akoafloor PB 4235-1 IVORY

About
Akoafloor PB 4235-1 ivory is a highly isotactic polyolefin manufactured from butene-1 monomer. The product provides excellent long term hydrostatic strength also at elevated temperatures combined with high flexibility. Akoafloor PB 4235-1 complies with requirements specified in ISO 15876, ISO 12230, DIN 16968/DIN 16969 and many other National Standards for PB-1 pipe applications. The grade is typically used for extrusion into pipe and injection moulding into fittings for nonpotable heating water applications. Akoafloor PB 4235-1 is available in ivory colour in pellet form. Akoafloor PB 4235-1 may not be used in the manufacture of pipe applications intended for sale or shipment to North America, without prior written approval by Seller for each specific product and application.&&

About

Akoafloor PB 4235-1 ivory is a highly isotactic polyolefin manufactured from butene-1 monomer. The product provides excellent long term hydrostatic strength also at elevated temperatures combined with high flexibility. Akoafloor PB 4235-1 complies with requirements specified in ISO 15876, ISO 12230, DIN 16968/DIN 16969 and many other National Standards for PB-1 pipe applications. The grade is typically used for extrusion into pipe and injection moulding into fittings for nonpotable heating water applications. Akoafloor PB 4235-1 is available in ivory colour in pellet form. Akoafloor PB 4235-1 may not be used in the manufacture of pipe applications intended for sale or shipment to North America, without prior written approval by Seller for each specific product and application.&&

Product Description
Supplier	LyondellBasell
Generic	PB
Material Status	Commercial: Active
Features	Good flexibility,Welding,High isotacticity,Heat Stabilized,Homopolymer
Availabilitys	Africa & Middle East ,Latin America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.930	g/cm³	ISO 1183
Melt Flow Rate
190℃，21.6kg	0.60	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
tensile strength
yield	17.0	MPa
fracture	30.0	MPa
Tensile strain
fracture	230	%	ISO 8986-2
Bending modulus	450	MPa	ISO 178

Process Conditions
injection	Nominal value	Unit	Test method
Squeeze description	Nominal value	Unit	Test method
Extrusion	Nominal value	Unit	Test method
Processing (melt) temperature	200 to 240	°C

Melt temperature	180 to 200	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.