AKROLOY® PA K17 FR black (5762)

About
AKROLOY® PA K17 FR black (5762) is a 35% glass fibre reinforced, halogen-free flame retardant PA 66 high temperature-alloy with high stiffness and strength as well as reduced moisture absorption. Parts in airospace and railway industry.

Product Description
Generic	PA66
Material Status	Commercial: Active
Features	Good Rigidity,Halogen free,Flame Characteristics,Low moisture absorption
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.50	g/cm³
Shrinkage rate
TD	0.90	%
MD	0.40	%
Water absorption rate
70℃，62% RH	1.4	%

MECHANICAL	Nominal value	Unit
Tensile modulus	12500	MPa
tensile strength
fracture	160	MPa
Tensile strain
fracture	2.5	%

IMPACT	Nominal value	Unit
Charpy Notched Impact Strength
23℃	12	kJ/m²
Charpy Unnotch Impact strength
23℃	60	kJ/m²

THERMAL	Nominal value	Unit
Hot deformation temperature
1.8 MPa, unannealed	250	℃
Melting temperature	260	℃

Electrical performance	Nominal value	Unit	Test method
Compared to the leakage tracing index
Solution A	600	V

FLAME CHARACTERISTICS	Nominal value	Unit
Burning rate
1 mm	< 100	mm/min
Flame retardant level
0.40 mm	V-0
0.80 mm	V-0
1.60 mm	V-0
2.00 mm	V-0
3.20 mm	V-0
Glowing wire flammability index
0.40 mm	960	℃
0.80 mm	960	℃
1.6 mm	960	℃
2.0 mm	960	℃
3.2 mm	960	℃
Igniting temperature of the hot wire
0.4 mm	800	℃
0.8 mm	800	℃
1.6 mm	775	℃
2 mm	775	℃
3.2 mm	775	℃

Supplementary information	Nominal value	Unit	Test method
Ash Content	35	%

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.