| About |
|---|
| AKROMID® C3 1 FR black (4361) is an unreinforced, heat stabilised, halogen-free flame retardant polyamide 6.6/6-Blend with good flow properties and suitable for moulded integral hinges. Switch parts and housings in the electric industry.&& |
| Product Description | |
|---|---|
| Generic | PA66/6 |
| Material Status | Commercial: Active |
| Features | Good liquidity,Halogen free,Flame Characteristics,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.16 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD | 1.1 | % | |
| MD | 1.1 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3300 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 75.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | > 10 | % | ISO 527-2/50 |
| Bending modulus | 3000 | MPa | ISO 178 |
| bending strength | 110 | MPa | ISO 178 |
| Fracture bending strain | 7.0 | % | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 3.0 | kJ/m² | |
| 23℃ | 4.0 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 90 | kJ/m² | |
| 23℃ | 100 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 210 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 70.0 | ℃ | ISO 75-2/A |
| Melting temperature | 260 | ℃ | DIN EN 11357-1 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | |||
| Solution A | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | |||
| 1 mm | < 100 | mm/min | FMVSS 302 |
| Flame retardant level | |||
| 0.40 mm | V-0 | ||
| 0.80 mm | V-0 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glowing wire flammability index | |||
| 0.40 mm | 960 | ℃ | |
| 0.80 mm | 960 | ℃ | |
| 1.6 mm | 960 | ℃ | |
| 3.2 mm | 960 | ℃ | |
| Igniting temperature of the hot wire | |||
| 0.4 mm | 775 | ℃ | |
| 0.8 mm | 775 | ℃ | |
| 1.6 mm | 775 | ℃ | |
| 3.2 mm | 775 | ℃ | |
| Extreme oxygen index | 34 | % | ISO 4589-2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. 2 mm/min |
| 4. 10°C/min |
| 5. >1 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |