| About |
|---|
| AKROTEK® PAEK CF 30 TM black (5217) is a 30% carbon fibre reinforced polyetherketoneketone with high flexural strength and good sliding properties as well as good tribological properties Elements in the automotive-, aeronautical-, industrial- and medical engineering that require high strength and high stiffness in a temperature environment above 150°C&& |
| Product Description | |
|---|---|
| Generic | PEKK |
| Material Status | Commercial: Active |
| Features | Good Rigidity |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.41 | g/cm³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 24600 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 230 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 1.3 | % | ISO 527-2/5 |
| Bending modulus | 23500 | MPa | ISO 178 |
| bending strength | 335 | MPa | ISO 178 |
| Fracture bending strain | 1.7 | % | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 38 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 8.0 MPa, unannealed | 205 | ℃ | ISO 75-2/C |
| 1.8 MPa, unannealed | > 280 | ℃ | ISO 75-2/A |
| Melting temperature | 340 | ℃ | DIN EN 11357-1 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. 2 mm/min |
| 4. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |