| About |
|---|
| Low/Medium Viscosity&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Low Viscosity |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | 3200 | MPa | |
| tensile strength | |||
| yield | 85.0 | MPa | |
| Tensile strain | |||
| yield | 4.0 | % | |
| Nominal tensile fracture strain | 20 | % | |
| Bending modulus | 2600 | MPa | |
| bending strength | 100 | MPa | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 5.0 | kJ/m² | |
| 23℃ | 8.0 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 无断裂 | ||
| 23℃ | 无断裂 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 150 | ℃ | |
| 1.8 MPa, unannealed | 60.0 | ℃ | |
| Melting temperature | 220 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | 9.0E-5 | 1/℃ | |
| TD | 1.0E-4 | 1/℃ | |
| Effective Thermal Diffusivity | 8.82E-8 | m²/s |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | |
| Dielectric strength | 30 | kV/mm | |
| Relative permittivity | |||
| 100 Hz | 3.40 | ||
| 1 MHz | 3.10 | ||
| Dissipation factor | |||
| 100 Hz | 6.5E-3 | ||
| 1 MHz | 0.017 | ||
| Compared to the leakage tracing index | — | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | |||
| 0.75 mm | V-2 | ||
| 1.5 mm | V-2 | ||
| Extreme oxygen index | 26 | % |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | |
| Shrinkage rate | |||
| TD | 1.1 | % | |
| MD | 1.1 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 10 | % | |
| Equilibrium, 23 ℃, 50% RH | 2.8 | % | |
| Viscosity number | 129 | cm³/g | |
| Melt density | 0.960 | g/cm³ | |
| Melt thermal conductivity | 0.23 | W/m/K | |
| Specific Heat Capacity of Melt | 2680 | J/kg/℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 230 to 235 | °C | |
| Barrel middle temperature | 235 to 250 | °C | |
| Barrel front temperature | 240 to 260 | °C | |
| Nozzle temperature | 240 to 270 | °C | |
| Processing (melt) temperature | 240 to 275 | °C | |
| Mold temperature | 50 to 80 | °C | |
| Injection speed | 中等偏快 | ||
| Back pressure | 3.00 to 10.0 | MPa | |
| Screw compression ratio | 2.5:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |