| Medium Viscosity, Film Extrusion, Lubricated&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Lubricating |
| Availabilitys | Europe |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| friction coefficient | ISO 8295 | ||
| With oneself – dynamic, casting thin films | 1.0 | ||
| Compared to itself – static, cast thin films | 1.2 | ||
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| Tensile modulus | |||
| 50 µ m, cast thin film | 455 | MPa | Internal Method |
| tensile strength | ISO 527-3 | ||
| MD, yield, 50 µ m, cast thin film | 31.0 | MPa | |
| MD, 50 µ m, cast thin film | 82.0 | MPa | |
| Tensile strain | |||
| MD, fracture, 50 µ m, cast thin film | 350 | % | ISO 527-3 |
| Pant tear resistance | |||
| MD, 50 µ m, cast thin film | 32.0 | N/mm | ISO 6383-1 |
| Water vapor transmittance | |||
| 23 ℃, 85% RH, 50 µ m, cast thin film | 35 | g/m²/24 hr | DIS 15106-1/-3 |
| Oxygen transfer rate | DIS 15105-1/-2 | ||
| 0% RH：23℃，50.0 µm | 26 | cm³/m²/bar/24 hr | |
| 85% RH：23℃，50.0 µm | 38 | cm³/m²/bar/24 hr |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Linear coefficient of thermal expansion | |||
| MD | 9.0E-5 | 1/℃ | ISO 11359-2 |
| Specific heat capacity | |||
| — | 1550 | J/kg/℃ | |
| Average: 20 to 150 ℃ | 2250 | J/kg/℃ |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| 50.0 µ m, cast thin film | 83.0 | % | Internal Method |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Puncture resistance | |||
| 50.0 µm | 13.0 | J/cm | Internal Method |
| RSV | 3.03 | Internal Method | |
| memo_intro |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Viscosity number | 196 | cm³/g | ISO 307 |
| Apparent viscosity of melt | |||
| 260℃ | 810 | Pa·s | Internal Method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |