| Supplier | DSM |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | High Viscosity,Lubricating,HB |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 9.5 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 2.5 | % | ISO 62 |
| Viscosity number | 244 | cm³/g | ISO 307 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 220 | ℃ | ISO 11357-3 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | IEC 60695-11-10, -20 | ||
| 1.5 mm | HB | IEC 60695-11-10, -20 | |
| 3.0 mm | HB | IEC 60695-11-10, -20 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 to 8.0 | hr | |
| Barrel rear temperature | 230 to 235 | °C | |
| Barrel middle temperature | 235 to 250 | °C | |
| Barrel front temperature | 240 to 260 | °C | |
| Nozzle temperature | 240 to 270 | °C | |
| Processing (melt) temperature | 240 to 275 | °C | |
| Mold temperature | 50 to 80 | °C | |
| Injection speed | Moderate-Fast | ||
| Back pressure | 3.00 to 10.0 | MPa | |
| Screw compression ratio | 2.5:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |