| About |
|---|
| Very High Viscosity, Lubricated, Film Extrusion&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | High Viscosity,Lubricating,Copolymer |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| friction coefficient | |||
| dynamic | 0.80 | ||
| static state | 1.4 | ||
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 465 | MPa | Internal Method |
| tensile strength | |||
| MD, yield | 34.0 | MPa | |
| MD, fracture | 94.0 | MPa | |
| Tensile strain | |||
| MD, fracture | 350 | % | ISO 527-3 |
| Trouser Tear（Parallel） | 32.0 | ISO 6383-1 | |
| Water vapor transmittance | |||
| 23℃，85% RH | 35 | g/m²/24 hr | DIS 15106-1/-3 |
| Oxygen transfer rate | |||
| 0% RH：23℃ | 23 | cm³/m²/bar/24 hr | |
| 85% RH：23℃ | 33 | cm³/m²/bar/24 hr |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 220 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD | 9.0E-5 | 1/℃ | ISO 11359-2 |
| Specific heat capacity | 1550 | J/kg/℃ |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Clarity | 85 | % | Internal Method |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Puncture resistance | 13.3 | J/cm | Internal Method |
| RSV（Formic Acid，1g/100ml） | 3.60 | Internal Method |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 9.0 | % | |
| Equilibrium, 23 ℃, 50% RH | 2.5 | % | |
| Viscosity number | 245 | cm³/g | ISO 307 |
| Apparent viscosity of melt | |||
| 260℃ | 2.25E+6 | mPa·s | Internal Method |
| mean specific heat | |||
| 20 to 150 ℃ | 2250 | J/kg/℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 230 to 235 | °C | |
| Barrel middle temperature | 235 to 250 | °C | |
| Barrel front temperature | 240 to 260 | °C | |
| Nozzle temperature | 240 to 270 | °C | |
| Processing (melt) temperature | 240 to 275 | °C | |
| Mold temperature | 50 to 80 | °C | |
| Injection speed | 中等偏快 | ||
| Back pressure | 3.00 to 10.0 | MPa | |
| Screw compression ratio | 2.5:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |