| Akulon® K222-KGV6是一种聚酰胺6（尼龙6）材料,含有的填充物为30% 玻璃纤维增强材料。 该产品在欧洲或亚太地区有供货,。 Akulon® K222-KGV6的主要特性有: 阻燃/额定火焰 Flame Retardant 热稳定剂 无卤素&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics,Low to no phosphorus content,Heat Stabilized,V-2 |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.44 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.90 | % | ISO 294-4 |
| MD | 0.55 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 5.6 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 1.5 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 6900 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 80.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 3.6 | % | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 43 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 180 | ℃ | ISO 75-2/A |
| Melting temperature | 220 | ℃ | ISO 11357-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | 525 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | IEC 60695-11-10, -20 | ||
| 0.75 mm | V-2 | IEC 60695-11-10, -20 | |
| 1.6 mm | V-2 | IEC 60695-11-10, -20 | |
| Glowing wire flammability index | IEC 60695-2-12 | ||
| 0.75 mm | 960 | ℃ | IEC 60695-2-12 |
| 1.6 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 0.75 mm | 725 | ℃ | IEC 60695-2-13 |
| 1.6 mm | 725 | ℃ | IEC 60695-2-13 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 to 8.0 | hr | |
| Barrel rear temperature | 225 to 235 | °C | |
| Barrel middle temperature | 230 to 240 | °C | |
| Barrel front temperature | 235 to 250 | °C | |
| Nozzle temperature | 235 to 255 | °C | |
| Processing (melt) temperature | 245 to 265 | °C | |
| Mold temperature | 50 to 80 | °C | |
| Injection speed | Moderate-Fast | ||
| Back pressure | 3.00 to 10.0 | MPa | |
| Screw compression ratio | 2.5:1.0 | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |