| About |
|---|
| 15% Glass Reinforced&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Availabilitys | Europe,North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Molding shrinkage | |||
| Parallel | 0.32 | % | ISO 294-4 |
| Normal | 0.96 | % | ISO 294-4 |
| Water Absorption | 7.6 | % | ISO 62 |
| Moisture Absorption | 2.3 | % | ISO 62 |
| Density | 1230 | kg/m³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | |||
| Dry | 6000 | MPa | ISO 527 |
| Wet Cond | 3500 | MPa | ISO 527 |
| Tensile Stress | |||
| Broken BRK, dry dry | 125 | MPa | ISO 527 |
| Broken BRK, wet Cond | 70 | MPa | ISO 527 |
| Elongation at Break | |||
| Dry | 3 | % | ISO 527-1,2 |
| Wet Cond | 12 | % | ISO 527-1,2 |
| Flexural Modulus | 5200 | MPa | ISO 178 |
| Flexural Strength | 170 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23 ℃, dry | 45 | kJ/m² | ISO 179/1eU |
| 23 ℃, moist cond | 80 | kJ/m² | ISO 179/1eU |
| -30 ℃, dry | 40 | kJ/m² | ISO 179/1eU |
| -30 ℃, moist cond | 40 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23 ℃, dry | 7 | kJ/m² | ISO 179/1eA |
| 23 ℃, moist cond | 15 | kJ/m² | ISO 179/1eA |
| -30 ℃, dry | 6 | kJ/m² | ISO 179/1eA |
| -30 ℃, moist cond | 6 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 220 | ℃ | ISO 11357-3 |
| Hot deformation temperature HDT | |||
| 1.80 MPa | 195 | ℃ | ISO 75-1/-2 |
| 0.45 MPa | 215 | ℃ | ISO 75-1/-2 |
| Coeff. of linear thermal expansion | |||
| Parallel | 0.3 | ×10-4/℃ | ISO 11359-2 |
| Normal | 0.8 | ×10-4/℃ | ISO 11359-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 1.5 mm | HB | calss | IEC 60695-11-10 |
| 3 mm | HB | calss | IEC 60695-11-10 |
| 0.75 mm | HB | calss | IEC 60695-11-10 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric Constant | |||
| Dry, 100Hz | 3.5 | IEC 62631-2-1 | |
| Wet Cond, 1MHz | 14 | IEC 62631-2-1 | |
| Dry, 100Hz | 4.7 | IEC 62631-2-1 | |
| Wet Cond, 1MHz | 4.5 | IEC 62631-2-1 | |
| Dissipation Factor | |||
| Dry, 100Hz | 55 | E-4 | IEC 62631-2-1 |
| Wet Cond, 1MHz | 1500 | E-4 | IEC 62631-2-1 |
| Dry, 100Hz | 180 | E-4 | IEC 62631-2-1 |
| Wet Cond, 1MHz | 1200 | E-4 | IEC 62631-2-1 |
| Volume Resistance | |||
| Dry | 1E13 | ohm·m | IEC 62631-3-1 |
| Wet Cond | 1E13 | ohm·m | IEC 62631-3-1 |
| Surface Resistivity | 1E14 | ohm | IEC 62631-3-2 |
| Dielectric Strength | |||
| Dry | 35 | kV/mm | IEC 60243-1 |
| Wet Cond | 25 | kV/mm | IEC 60243-1 |
| Compared Tracking Index | 600 | V | IEC 60112 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature Zone 1 | 255 to 265 | °C | |
| Middle Temperature Zone 2 | 265 to 275 | °C | |
| Front Temperature Zone 3 | 265 to 280 | °C | |
| Nozzle temperature | 260 to 280 | °C | |
| Melt Temperature | 250 to 285 | °C | |
| Mold Temperature | 50 to 80 | °C | |
| Injection speed | 中等偏快 | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |