| About |
|---|
| Flame Retardant (halogen free), Heat Stabilized, Laser-Markable Special Features: Contains release agent Heat stabilized or stable to heat Laser markable Akulon® is our family of high performance polyamide 6 and polyamide 66 materials, used by customers across the world in applications ranging from automotive, electronics & electrical, to furniture and packaging. We offer Akulon® grades for injection molding, blow molding and extrusion (including barrier film, stock shapes, convoluted tubes, and mono and multi filament). In molded parts the material offers an excellent balance of easy design and processing with outstanding mechanical properties over a wide temperature range and in diverse conditions. Meanwhile for extrusion the strength, resilience and easy processing of Akulon® sets the market standards.&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics,Laser engraving,Heat Stabilized,V-0 |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.18 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD | 1.0 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 9.0 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 2.5 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3800 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 80.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 3.5 | % | ISO 527-2 |
| Nominal tensile fracture strain | 8.0 | % | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 5.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 55 | kJ/m² | ISO 179/1eU |
| 23℃ | 60 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 80.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 200 | ℃ | ISO 75-2/B |
| Melting temperature | 220 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| TD | 9.0E-5 | 1/℃ | ISO 11359-2 |
| MD | 9.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | — | ohms | IEC 60093 |
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 30 | kV/mm | IEC 60243-1 |
| Relative permittivity | IEC 60250 | ||
| 100 Hz | 3.30 | IEC 60250 | |
| 1 MHz | 3.20 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 9.0E-3 | IEC 60250 | |
| 1 MHz | 0.020 | IEC 60250 | |
| Compared to the leakage tracing index | — | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | IEC 60695-11-10, -20 | ||
| Flame retardant grade (0.38 mm) | V-0 | IEC 60695-11-10, -20 | |
| 1.5 mm | V-0 | IEC 60695-11-10, -20 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 to 8.0 | hr | |
| Barrel rear temperature | 225 to 230 | °C | |
| Barrel middle temperature | 230 to 235 | °C | |
| Barrel front temperature | 230 to 240 | °C | |
| Nozzle temperature | 230 to 250 | °C | |
| Processing (melt) temperature | 245 to 255 | °C | |
| Mold temperature | 50 to 80 | °C | |
| Injection speed | Moderate-Fast | ||
| Back pressure | 3.00 to 10.0 | MPa | |
| Screw compression ratio | 2.5:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |