| About |
|---|
| Akulon®是高性能PA6和PA66家族，客户遍布全球，广泛应用于汽车、电子电气、家具、包装等行业。&&我们提供注塑级、吹塑级和挤出级的Akulon®牌号，其中挤出级包括阻隔膜、棒材、波纹管和单层多层膜。&&用此材料注塑时，在设计简单和卓越的机械性能间能达到完美的平衡，应用种类多，温度范围广。用作挤出时，Akulon®的强度、回弹性和加工简便都是市场标杆。 |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good stripping performance |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.34 | g/cm³ | ISO 1183 |
| Melt volume flow velocity | 8 / * | cm³/10min | ISO 1133 |
| temperature | 260 / * | °C | ISO 1133 |
| load | 2.16 / * | kg | ISO 1133 |
| Melt Index (MFI) | 12 / * | g/10min | ISO 1133 |
| MFI test temperature | 260 / * | °C | ISO 1133 |
| MFI testing load | 2.16 / * | kg | ISO 1133 |
| Shrinkage rate | |||
| MD | 1.1 / * | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 9400 / – | MPa | ISO 527-1-2 |
| Fracture stress | 165 / – | MPa | ISO 527-1/-2 |
| Tensile strain | |||
| fracture | 2.8 / – | % | ISO 527-1/2 |
| Bending modulus | 8500 / – | MPa | ISO 178 |
| bending strength | 240 / – | MPa | ISO 178 |
| Other performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Water absorption rate | 6.3 / * | % | ISO 62 |
| Moisture absorption rate | 2.1 / * | % | Sim. to ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| -30℃ | 60 / – | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| -30℃ | 8 / – | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | |||
| 10℃ / min | 220 / * | ℃ | ISO 11357-1/-3 |
| Hot deformation temperature | |||
| 1.8 MPa | 200 / * | ℃ | ISO 75-1/2 |
| Melt density | 1150 / * | kg/m³ | – |
| Melt thermal conductivity | 0.27 / * | W/(m K) | – |
| Specific heat of melt | 2110 / * | J/(kg K) | – |
| Thermal diffusivity | 1.12E-7 / * | m²/s | – |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |