| About |
|---|
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA66 |
| Material Status | Commercial: Negative |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1390 | kg/m³ | ISO 1183 |
| Mold shrinkage rate | |||
| parallel | 0.3 | % | ISO 294-4 |
| normal | 1.04 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 10000 | MPa | ISO 527-1/-2 |
| Tensile stress | |||
| fracture | 140 | MPa | ISO 527-1/-2 |
| Tensile strain | |||
| fracture | 3.2 | % | ISO 527-1/-2 |
| Bending modulus | 8650 | MPa | ISO 178 |
| bending strength | 225 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy impact strength | |||
| 23℃ | 65 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | 9 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | |||
| 10°C/min | 260 | ℃ | ISO 11357-1/-3 |
| combustion performance | |||
| 1.5 mm | V-0 | calss | IEC 60695-11-10 |
| 3.0 mm | V-0 | calss | IEC 60695-11-10 |
| 0.4 mm | V-0 | calss | IEC 60695-11-10 |
| 0.75 mm | V-0 | calss | IEC 60695-11-10 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Glowing wire flammability index | 960 | ℃ | IEC 60695-2-12 |
| Thickness (1) Test | 0.75 | mm | IEC 60695-2-12 |
| Glowing wire flammability index | 960 | ℃ | IEC 60695-2-12 |
| Thickness (2) testing | 3 | mm | IEC 60695-2-12 |
| Igniting temperature of the hot wire | 800 | ℃ | IEC 60695-2-13 |
| Thickness (1) Test | 0.75 | mm | IEC 60695-2-13 |
| Igniting temperature of the hot wire | 825 | ℃ | IEC 60695-2-13 |
| Thickness (2) testing | 3 | mm | IEC 60695-2-13 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Electrical strength | 40 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |