| About |
|---|
| 30% Glass Reinforced, Heat Stabilized, Flame Retardant, High Flow&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,Heat Stabilized,High liquidity |
| Availabilitys | Europe,North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.59 | g/cm³ | ISO 1183 |
| Water Absorption | 4.5 | % | ISO 62 |
| Moisture Absorption | 1.3 | % | ISO 62 |
| Molding shrinkage | |||
| MD | 0.21 | % | ISO 294-4 |
| TD | 0.77 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | 11500/7000 | MPa | ISO 527-1/-2 |
| Tensile Strength | |||
| Broken BRK | 150/100 | MPa | ISO 527-1/-2 |
| Tensile Strain | |||
| Broken BRK | 2.5/5 | % | ISO 527-1/-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 60/60 | kJ/m² | ISO 179/1eU |
| -30℃ | 60/60 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | 13/15 | kJ/m² | ISO 179/1eA |
| -30℃ | 12/12 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 220 | ℃ | ISO 11357-1/-3 |
| Hot deformation temperature HDT | |||
| 1.80 MPa | 205 | ℃ | ISO 75-1/-2 |
| 0.45 MPa | 215 | ℃ | ISO 75-1/-2 |
| Coeff. of linear thermal expansion | |||
| MD | 0.2 | E-4/℃ | ISO 11359-1/-2 |
| TD | 1.1 | E-4/℃ | ISO 11359-1/-2 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric Constant | |||
| 100 Hz | 3.5/10 | IEC 60250 | |
| 1 MHz | 3.4/4 | IEC 60250 | |
| Dissipation Factor | |||
| 100 Hz | 60/3000 | E-4 | IEC 60250 |
| 1 MHz | 120/700 | E-4 | IEC 60250 |
| Volume Resistance | 1.0E+13 / 1.0E+11 | Ohms*m | IEC 60093 |
| Surface Resistivity | 1.0E+14 | Ohms | IEC 60093 |
| CTI | 325 | V | IEC 60112 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature Zone 1 | 230 to 250 | °C | |
| Middle Temperature Zone 2 | 230 to 260 | °C | |
| Front Temperature Zone 3 | 230 to 260 | °C | |
| Nozzle temperature | 250 to 280 | °C | |
| Melt Temperature | 245 to 270 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection speed | 中等偏快 | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |