| About |
|---|
| Alathon H5618 provides easy processing characteristics and exhibits excellent toughness properties and color as well as low odor and good processing stability. Typical applications include housewares, containers, caps and closures.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good flexibility,Food contact compliance,Low odor |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.956 | g/cm³ | ASTM D1505 |
| Apparent density | 0.53 to 0.59 | g/cm³ | ASTM D1895 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 18 | g/10min | ASTM D1238 |
| Spiral flow length | 29.7 | cm | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 69 | ASTM D2240 | |
| Tensile modulus | ASTM D638 | ||
| — | 1050 | MPa | ASTM D638 |
| 1% secant | 845 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 24.0 | MPa | ASTM D638 |
| yield | 29.2 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 62 | % | ASTM D638 |
| yield | 8.0 | % | ASTM D638 |
| Bending modulus | ASTM D790 | ||
| — | 1490 | MPa | ASTM D790 |
| 1% secant | 1410 | MPa | ASTM D790 |
| 2% secant | 1180 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 31 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| -18℃ | No Break | ASTM D4812 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 72.8 | ℃ | ASTM D648 |
| Embrittlement temperature | < -76.1 | ℃ | ASTM D746 |
| Vicat Softening Temp | 124 | ℃ | ASTM D1525 |
| Melting peak temperature | 130 | ℃ | ASTM D3418 |
| Crystallization peak temperature | |||
| DSC | 115 | ℃ | ASTM D3418 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Barrel rear temperature | 232 | °C | |
| Barrel middle temperature | 243 | °C | |
| Barrel front temperature | 246 | °C | |
| Nozzle temperature | 246 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 23°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |