| About |
|---|
| Alathon L5005 is a high molecular weight high density copolymer that provides broad bimodal molecular weight distribution, high stiffness and good heat seal response and strength. L5005 is selected by customers for use in merchandise bags, grocery sacks, trash can liners, produce bags and roll stock.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | HMW-HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good heat sealing,Food contact compliance,High molecular weight,Copolymer |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.949 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.060 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Secant modulus | |||
| TD | 1050 | MPa | ASTM D882 |
| MD | 945 | MPa | ASTM D882 |
| tensile strength | |||
| TD, fracture | 57.2 | MPa | ASTM D882 |
| TD, yield | 29.0 | MPa | ASTM D882 |
| MD, fracture | 84.1 | MPa | ASTM D882 |
| MD, yield | 34.5 | MPa | ASTM D882 |
| Tensile strain | |||
| TD, fracture | 390 | % | ASTM D882 |
| MD, fracture | 320 | % | ASTM D882 |
| Drop hammer impact | 340 | g | ASTM D1709 |
| Elmandorf tear strength | |||
| MD | 11 | g | ASTM D1922 |
| tear strength | |||
| TD | 76 | g | ASTM D1922 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 23°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |