| About |
|---|
| Alathon L5485 is a medium molecular weight, high density polyethylene copolymer for use in blown film applications. Typical applications include general-purpose HDPE film applications such as overwrap, laminating base films, food packaging and oriented tapes.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | MMW-HDPE |
| Material Status | Commercial: Active |
| Features | Food contact compliance,Copolymer |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.954 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.85 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Secant modulus | |||
| TD | 1240 | MPa | ASTM D882 |
| MD | 931 | MPa | ASTM D882 |
| tensile strength | |||
| TD, fracture | 23.4 | MPa | ASTM D882 |
| TD, yield | 26.2 | MPa | ASTM D882 |
| MD, fracture | 54.5 | MPa | ASTM D882 |
| MD, yield | 25.5 | MPa | ASTM D882 |
| Tensile strain | |||
| TD, fracture | 750 | % | ASTM D882 |
| MD, fracture | 700 | % | ASTM D882 |
| Elmandorf tear strength | |||
| MD | 32 | g | ASTM D1922 |
| tear strength | |||
| TD | 1000 | g | ASTM D1922 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 199 to 210 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 23°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |