| About |
|---|
| ALCOM® AWL 109/10 WT1218-11LB is a Polycarbonate + ABS (PC+ABS) product filled with 10% filler. It is available in Asia Pacific, Europe, or North America. Applications of ALCOM® AWL 109/10 WT1218-11LB include lighting applications, automotive and reflectors. Characteristics include: Flame Rated RoHS Compliant Copolymer Heat Stabilizer&& |
| Product Description | |
|---|---|
| Supplier | ALBIS |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | High reflectivity,Heat Stabilized,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 220℃，10 kg | 17.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD：24 hrs | 0.10 | % | ISO 294-4 |
| MD：24 hrs | 0.30 | % | ISO 294-4 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 20 | kJ/m² | ISO 179-1eA |
| Charpy Unnotch Impact strength | 无断裂 | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 100 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 109 | ℃ | ISO 306 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 | |
| Fire resistance performance | |||
| 2.00 mm | passed | FMVSS |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Tristimulus Value | |||
| Y10 of Reflection | 85 | % | DIN 5033 |
| Y10 of Transmittance：500.0 µm | 0.20 | % | ISO 13468 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 115 | MPa | ISO 2039-1 |
| Tensile modulus | 2500 | MPa | ISO 527-2 |
| tensile strength | ISO 527-2 | ||
| yield | 50.0 | MPa | ISO 527-2 |
| fracture | 39.0 | MPa | ISO 527-2 |
| Tensile strain | ISO 527-2 | ||
| yield | 3.0 | % | ISO 527-2 |
| fracture | 13 | % | ISO 527-2 |
| Bending modulus | 2500 | MPa | ISO 178 |
| bending strength | 78.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | |||
| Desiccant desiccant | 80 | °C | |
| Hot air dryer | 80 | °C | |
| Drying time | |||
| Desiccant desiccant | 3.0 to 6.0 | hr | |
| Hot air dryer | 2.0 to 4.0 | hr | |
| Processing (melt) temperature | 230 to 260 | °C | |
| Mold temperature | 50 to 80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. DIN 75200 |
| 3. Y10 of Reflection |
| 4. Y10 of Transm. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |