| About |
|---|
| ALCOM® AWL 109/15 WT1217-11LB是一种聚碳酸酯+丙烯腈丁二烯苯乙烯(PC+ABS)产品,含有的填充物为15% 填料。 它,在北美洲、欧洲或亚太地区有供货。 ALCOM® AWL 109/15 WT1217-11LB的应用领域包括汽车行业 和 照明设备。 特性包括: 阻燃/额定火焰 符合 REACH 标准 通过 ROHS 认证 热稳定剂&& |
| Product Description | |
|---|---|
| Supplier | ALBIS |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | High reflectivity,Heat Stabilized,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.21 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 220℃，10 kg | 17.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| — | 0.30 to 0.60 | % | ISO 294-4 |
| TD：24 hrs | 0.50 | % | ISO 294-4 |
| MD：24 hrs | 0.60 | % | ISO 294-4 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 13 | kJ/m² | ISO 179-1eA |
| Charpy Unnotch Impact strength | 100 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 100 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 109 | ℃ | ISO 306 |
| Ball pressure test | |||
| 100℃ | 通过 | IEC 60695-10-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 | |
| Glowing wire flammability index | |||
| 2.0 mm | 550 | ℃ | IEC 60695-2-12 |
| Fire resistance performance | |||
| 2.00 mm | passed | FMVSS |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Tristimulus Value | |||
| Y10 of Reflection | 92 | % | DIN 5033 |
| Y10 of Transmittance：500.0 µm | 0.40 | % | ISO 13468 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 115 | MPa | ISO 2039-1 |
| Tensile modulus | 2700 | MPa | ISO 527-2 |
| tensile strength | ISO 527-2 | ||
| yield | 50.0 | MPa | ISO 527-2 |
| fracture | 39.0 | MPa | ISO 527-2 |
| Tensile strain | ISO 527-2 | ||
| yield | 3.0 | % | ISO 527-2 |
| fracture | 13 | % | ISO 527-2 |
| Bending modulus | 2700 | MPa | ISO 178 |
| bending strength | 75.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | |||
| Desiccant desiccant | 80 to 90 | °C | |
| Hot air dryer | 80 to 90 | °C | |
| Drying time | |||
| Desiccant desiccant | 3.0 to 6.0 | hr | |
| Hot air dryer | 2.0 to 4.0 | hr | |
| Processing (melt) temperature | 230 to 260 | °C | |
| Mold temperature | 50 to 80 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |